Our consultant will save your time!
Nicholas
sales department
+38 (050) 369-66-30
FEATURE
Titanium alloy ВТ16 refers to a group of wrought α+β-alloys. The alloy was developed by Viama. Production of normalized GOST 19807−74, 90013−81 OST. The doping with aluminum of 1.8% to 3.8%, molybdenum 4.5 to 5.5%, V 4−5%.gives long products manufacture of optimal technological properties. Hardened by heat treatment. The optimal combination is achieved by quenching and aging.
Percentage composition of the brand ВТ16 according to GOST 19807−91
| Al | C | Si | Fe | Mo | Zr | N | O | H | V | Ti |
|---|---|---|---|---|---|---|---|---|---|---|
| 1,8−3,8 | ≤0,1 | ≤0,15 | ≤0,25 | 4.5 to 5.5 | ≤0.3 mm | ≤0,05 | ≤0,15 | ≤0,015 | 4−5 | 84,85−89,7 |
The Titan is a basis; it is the percentage specified in the table. Limit short-term strength of rolled reaches 1300−1400 MPa. Hardness after quenching and aging 30−40 MPa. The density of 4.68 g/cm3.
| DOS. quality | Use | Note |
| Alloying of aluminum, vanalism, zirconium and molybdenum increases the heat resistance and strength in comparison with rafting VT6. Working t.°+ 350°. The optimum combination of qualities provides a double and isothermal annealing. The content of β-phase in the annealed alloy = 10%. Hardening is achieved by aging and quenching. | Fastener compressors, valves, fans, screw the details. | Deformed in the hot state. Processed with pressure and welded worse than VT6. |
buy at best price
A wide range of titanium semis brand ВТ16 always available in stock, LLC «_". Products made of titanium alloys, presented on our site, are offered at the price of the manufacturer without including the additional cost and affordable way of placing order and choosing the most suitable shipping option will ensure maximum comfort to the buyer. A huge variety of titanium mill products, we will pick up the necessary material to solve any most complicated industrial tasks.