The grade VT1−0 contains technically pure titanium, in which impurities account for about 0.5%. Leaf rolling of this brand is distinguished by high corrosion and chemical resistance, ductility, heat resistance, minimum coefficient of thermal expansion, small ud. Weight (4.5 g / cm 3). Material VT1−0 is biologically inert, meets the strictest sanitary and hygienic requirements
| Thickness mm | Name | Heat treatment | Plasticity δ% | Strength (MPa) | KCU J / cm³ |
|---|---|---|---|---|---|
| 0.3 — 0.4 | Sheet | Delivery status | > 25 | 392 — 540 | --- |
| 0.3 — 0.5 | — «- | Annealing | .> 25 | > 400 | --- |
| 0.5 — 1.8 | — «- | Delivery status | > 30 | 392 — 540 | --- |
| 2 — 6 | — «- | — «- | > 25 | 392 — 540 | --- |
| 6.5 — 10 | — «- | — «- | > 20 | 392 — 540 | --- |
| 16 | — «- | Hot-rolled | 31.2 | 467 | --- |
| 20 | — «- | Hot-rolled | 30.0 | 461 | --- |
| 25 | — «- | — «- | 30.0 | 480 | --- |
| 2 | — «- | Annealing | 51 | 338 | --- |
| 0.3 — 0.5 | Tape | — «- | > 45 | 343 — 490 | --- |
| 0.55 — 1.5 | — «- | — «- | > 35 | 343 — 490 | --- |
| 0.05−0.08 | Foil | — «- | --- | > 400 | --- |
| 0.08 | Foil, small grain | — «- | 18 — 26 | 540 — 600 | --- |
| 0.05−0.03 x 90 mm | Foil | Vacuum annealing | 31.2 | 510 | --- |
| 0.08 | Foil, large grain | Annealing | 8 — 10 | 640 — 700 | --- |
The annealing temperature of the sheet and tape VT1−0 530 — 565 ° C, t ° of incomplete annealing is about 480 ° C
limitations
High labor intensity of production. Hot titanium reacts actively with atmospheric gases. Therefore, it melts only in inert gases or in a vacuum, VT1−0 is difficult to cut hard, its strength (400−500 MPa), is not considered high enough. For comparison, the strength of VT20 is more than 1000 MPa.
| Physical properties | |
|---|---|
| The temperature at which these characteristics were obtained t ° C | 20 ° С |
| Coefficient of linear thermal expansion α [1 / degree] | 8.2 x 10 -6 |
| Density [g / cm 3 ] | 4.45 |
| Modulus of elasticity of the first kind, E [MPa] x10 -5 | 1.12 |
| Specific heat at 20 ° C С [kJ / (kg · deg)] | 0.54 |
| Thermal conductivity K [W / (m · K)] | 307.3 |
| Coefficient of thermal conductivity), l [W / (m · deg)] | 18.85 |
Application of
Power engineering, petrochemistry, aircraft construction, rocket engineering, shipbuilding, design. High corrosion resistance, ductility, heat resistance, small ud. Weight (4.5 g / cm 3) make sheet rolling VT1−0 almost the ideal material for stamped parts, which make it possible to facilitate the design without loss of reliability. Compliance with the strictest sanitary and hygienic requirements allows the use of VT1−0 for the manufacture of surgical instruments, as well as plates, screws, pins for the needs of orthopedics, as well as prosthetic joints, dental crowns and bridges, etc.
BUY AT THE OPTIMAL PRICE
The brand VT1−0 is presented in the warehouse of LLC «_" with a full range of products that will satisfy any customer. The optimal price category and full compliance with the requirements of technical documentation will ensure the reliability and economic efficiency of production Individual work with each customer regardless of the purchase price is the motto of our work Since the company was founded.