ХН75ТБЮ, ЭИ869 round, wire, tube, sheet, strip

RELEVANCE

Generally, alloys based on Nickel, despite its relatively high cost, have a set of unique properties that compensate for the initial costs. Such properties include high corrosion resistance on the background of good machinability of the material, a significant resistance, allowing the use of articles made of Nickel alloys under the impact of the Assembly to elevated temperature regimes. So today, materials of this type are deservedly gained increased popularity and constant demand in many industries in connection with which their trade is constantly usovershenstvuetsya and growing.

CHARACTERISTICS OF THE ALLOY

The basic properties of a material such as alloy ХН75ТБЮ directly depend on the chemical composition, the percentage content of the constituent elements. So Nickel has led to the inertia of the steel to the action of aggressive industrial environments and high heat resistance, preventing the destruction of this alloy under the action of high temperature modes of operation. These useful qualities have determined the scope of application of this alloy. Made a different attachment, rotary members, a flat spring type, the details of the combustion chamber and the constructive part of the pipeline systems, whose work is limited to temperature index of 950 degrees Celsius. Another important feature is the good weldability of the alloy in connection with which the semi-finished products of the brand ХН75ТБЮ can be used for the manufacture of welded structures of any complexity.

COMPOSITION

The percentage of chemical elements
C Fe Mn P Ce Si S Ni Cr Ba Al
to 0.1 19,13−27,4 to 0.3 to 0.02 0.03 to 0.8 to 0.02 55−58 15−18 to 0.1 2,6−3,5

Technological parameters

Weldability The necessary operations
The material is of type alloys difficult to weld Before welding contact surface has warmed up to two hundred or three hundred degrees. After welding, to improve the characteristics of the suture zone of the prefabricated subjected to high temperature annealing.
Alloys limited welded type Qualitative welded connection, maybe get after preheating contacting surfaces to one hundred or one hundred and twenty degrees Celsius, and conducting a final heat treatment suture zone, after the completion of welding works
Raw materials, not having restrictions on welding Prior training is not required for high-quality welding
Mechanical properties
Name characteristics The symbol Numeric value
Rolled sheet according to GOST 24982−81
The limit of proportionality (flow rate for residual deformation type), MPa sT 345−390
Short-term strength (limit value), MPa blower SB 740
The rate of elongation at the terminal force, % d5 35
Heat treatment Annealing at temperatures from 1050 to 1090ºC

Physical properties

Name characteristics The numerical value of the parameter
The modulus of elasticity (E), MPa 1,69 2,1
Temperature measurements (T), ºC 900 800 700 600 500 400 300 200 100 20
The coefficient of linear expansion measured at a temperature of 200ºC (ах106), 1/deg 15,88 15,18 15,11 14,59 14,22 14,2 13,42 13,08 12,28
Heat (I), W/(mgrad) 47,4 40,2 34,5 29,3 24 19,6 15,9 13 10,5

BUY AT BEST PRICE

The best combination of price and quality of alloy ХН75ТБЮ has led to a high demand for semi-finished products made of this steel. A wide range of products and a convenient method of ordering will make a purchase from us as comfortable as possible. Full conformity with requirements of normative documentation, prompt order processing and delivery in the shortest possible time in any region of the country or abroad, has long won the trust of many loyal clients. Due to the relatively low cost and wide model range of semi-finished alloy ХН75ТБЮ enjoys continued popularity in all spheres of production.

Our consultant will save your time!

Vitaliy

Vitaliy

sales department

+38 (095) 209-60-73