Heat-resistant sheet hire of mark 10X17H13M2T made from high corrosion-resistant austenitic steel. The basis of the raw materials are iron, Nickel and chromium Additives such chemical elements as manganese, titanium and silicon — stabilized material, which is an outstanding representative of stainless alloys. A wide range of sheet metal, brand 10X17H13M2T produced modern industry allows equipment long time to work at temperatures up to 600 degrees with no loss of technological qualities.

The percentage composition of the alloy according to the 10X17H13M2T GOST 5632−72.

Mo C Si Cr Ni Ti Mn P S Fe
2−3 ≤0,1 ≤0,8 16−18 12−14 ≤0,7 ≤2 ≤0,035 ≤0,02 basis

Hot rolled sheet is carried out at an initial temperature +1180°C with a gradual decrease to +850°C. Cooling in air. Sheet production normalized following GOST: 7350−77, 4405−75.


Welded structures are not exposed to shock loads, operating at t up to 600 °C, welded structures operating under conditions of chemical production in contact with aggressive environment, acetic, phosphoric acid — chemical reactors, evaporators, tanks, etc.


Sheet 10X17H13M2T presents in stock, LLC «_" the full range of products that will satisfy any customer. Optimum price category and full compliance with the requirements of technical documentation will allow to provide the reliability and economic efficiency of production. Individual work with every customer regardless of the purchase price is our motto since the founding of the company.